Characteristic:
Two-component filler on the basis of hydroxy-acrylic resin. It has excellent filling properties as well as good adhesion to the puttied surface. It is recommended to use under one and two-component acrylic topcoats, synthetic or water-borne. Destined for manual/machine treatment with sanding dry and wet materials. This filler is particularly suitable for filling surfaces of bodies in automotive industry, steel structures protected with anticorrosion primers. This is a perfect product for filling steel and polyester-glass surfaces, previously repaired with polyester putties and hard plastics, used in motorization.

Application:
The surface must be cleaned, dry, degreased and matted. Mixing ratio: 5:1 by volume and add thinner for acrylic products 20 - 25 % vol.. Mix thoroughly. Apply with a spray gun with nozzle diameter 1,6 - 1,8 mm in 2 - 3 normal coats with 8 - 10 min. flash off at 20°C between the coats. Drying 30 min. at 60°C or 5 - 7 hours at 20°C. Sand dry with P320 - P400 or wet with P800 - P1200.

Technical data:

• Efficiency: 5 m²/l
• Density: 1,56 - 1,58 g/cm³
• Shelf-life: 12 months
• VOC content: 2004/42/IIB(c)(540)<540
• Spray viscosity: 5 - 30 sec. at 20°C, Ford cup 4 mm
• Pot life: up to 2h at 20°C
• Spray gun: Nozzle diameter: 1,6 - 1,8 mm
• Application: 2-3 normal coats
• Flash-off: 8 - 10 min. at 20°C
• Drying time: 30 min. at 60°C, 5-7 h at 20°C